PolyWood™ Filament - 1.75mm

PolyMaker

This Specialty family provides unique filaments from Polymaker to unlock new 3D printing applications.

PolyWood™ is a wood mimic filament without actual wood powder, which removes all risks of nozzle clogs. PolyWood™ is made entirely with PLA using a special foaming technology. It exhibits the same density and appearance as wood.

Polymaker Polywood Wood 3D printing Filament Canada

PolyWood™ features Polymaker's Jam-Free™ technology and Polymaker's Stabilized Foaming™ technology:

Jam-Free™ technology improves the heat stability of Polymaker’s PLA filaments with softening temperatures over 140 °C. As a result, Polymaker’s PLA filaments show minimal softening in the “cold end” and can melt rapidly once entering the heating zone, leading to excellent printing quality with zero risk of nozzle jams.

Polymaker Polywood Wood 3D printing Filament Canada

Stabilized Foaming™ technology is used to produce foamed filaments, whose foam structure can survive the printing process and be inherited by the printed parts. This enables light weight 3D printed parts with unprecedented surface finish.

Tensile Strength:
23.2 ± 0.4 Mpa

Bending Strength:
52.9 ± 0.3 Mpa

Charpy Impact Strength:
2.1 ± 0.2 kJ/m2

Tensile Strength:
23.2 ± 0.4 Mpa

Bending Strength:
52.9 ± 0.3 Mpa

Charpy Impact Strength:
2.1 ± 0.2 kJ/m2

 3d filament net weight NET WEIGHT: 0.6 KG (1.3 LB)

3d printing temperature guideline Printing
Temperature:

Notes:

190°C - 210°C

Nozzle Temperature:
190˚C – 210˚C

Printing Speed:
35mm/s – 50mm/s

Bed Temperature:
25˚C – 60˚C

Bed Surface:
Glass with glue, blue tape, BuilTak®

Cooling Fan:
ON

Drying Settings:
70˚C for 8h

Recommended Support Materials:
PolyDissolve™ S1